Mass‐Spectrometric Observation of Counter Anion Production in SU‐8 Exposed to UV Light and its Use for Dill C Parameter Determination

Photopolymerization is a phenomenon that is the basis of much of today's microfabrication technology and intense research is conducted to improve its control and the characteristics of end products for a variety of applications. The design of microscopic structures often relies on the accurate knowledge and modeling of photopolymer's behavior upon exposure, i.e. the Dill parameters, for each radiation species of interest and therefore the development of flexible characterization techniques is of great importance. SU‐8 is a popular compound that is representative of a whole class that relies on cationic polymerization, where an acid is obtained via photolysis of an onium salt during exposure. Here we report on the observation of SbF₆^? via laser desorption mass spectrometry on SU‐8 exposed to UV light at the wavelength of 365 nm and demonstrate that the yield of this counter‐anion as a function of exposure is consistent with the Dill C parameter value available in the literature. © 2019 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2019 , 57, 967–972     

单宁酸/两性离子改性油-水分离膜的制备及性能

以不锈钢网为基材, 利用单宁酸对不锈钢网进行表面预处理并功能化接枝两性离子基团, 制备了新型亲水和水下超疏油的单宁酸/两性离子改性油-水分离膜(TA-ZW-SSM). 利用X射线光电子能谱仪(XPS)、 扫描电子显微镜(SEM)及接触角测量仪等表征了其化学结构、 形态和润湿性. 研究结果表明, 两性离子基团通过化学键接枝在单宁酸预处理的不锈钢网表面. 油-水分离实验结果表明, 对于不同类型的油-水混合物, 本文制备的超亲水和水下超疏油特性的TA-ZW-SSM可实现重力驱动的高效油-水分离, 并具有较好的化学稳定性及再循环性.     

An insight into the potent antioxidant activity of a dithiocarbohydrazone appended cis-dioxidomolybdenum (VI) complexes

In search of antioxidants with enriched potency, the present study focus on the design and synthesis of a dithiocarbohydrazone, H₃TCL derived from thiocarbohydrazide and 3-ethoxysalicylaldehyde and its coordination complexes with molybdenum, viz, [MoO₂(HTCL)D] ( 1 – 2 ) (where D = methanol ( 1 ), DMSO ( 2 )) and [MoO₂(HTCL)D]·DMF (where D = H₂O ( 3 )). The synthesized compounds were characterised by elemental analysis, spectroscopic techniques (FT-IR, UV–vis and ¹H-NMR), conductivity measurements and cyclic voltammetry. Moreover the solid state structures of all the three complexes were established by single crystal X-ray diffraction analysis as mononuclear neutral species in which the molybdenum centre assumes a distorted octahedral geometry. The dithiocarbohydrazone binds to the molybdenum centre through its phenolate oxygen, O(1), azomethine nitrogen, N(1) and thioenolate sulfur, S(1) in a dianionic tridentate mode. The assessment of intermolecular contacts in the crystal arrangement was quantified using Hirshfeld surface analysis. Further the antioxidant potential of the dithiocarbohydrazone, H₃TCL and its molybdenum complexes 1 – 3 were evaluated using 1,1-diphenyl-2-picrylhydrazyl(DPPH), 2,2′-azinobis-3-ethylbenzothiazoline-6-sulfonic acid (ABTS) and total antioxidant assays. The antioxidant activities were then compared with standard antioxidant, L-ascorbic acid. The antioxidant potential of the synthesized compounds were then validated by molecular docking studies. Molecular modelling study was achieved to evaluate the recognition of target compound at the binding pocket of the human antioxidant enzyme, 3MNG. The docking results showed that the complexes selectively bond to the vital amino acids present in the binding pocket of the target enzyme, 3MNG.     

Composite host lattices of 4,4′‐sulfonyldibenzoate water/boric acid in two tetrapropylammonium inclusion compounds

Two novel inclusion compounds of 4,4′‐sulfonyldibenzoate anions and tetrapropylammonium cations with different ancillary molecules of water and boric acid, namely bis(tetrapropylammonium) 4,4′‐sulfonyldibenzoate dihydrate, 2C₁₂H₂₈N⁺·C₁₄H₈O₆S²⁻·H₂O ( 1 ), and bis(tetrapropylammonium) 4,4′‐sulfonyldibenzoate bis(boric acid), 2C₁₂H₂₈N⁺·C₁₄H₈O₆S²⁻·2H₃BO₃ ( 2 ), were prepared and characterized using single‐crystal X‐ray diffraction. In the two salts, the host 4,4′‐sulfonyldibenzoic acid molecules, which are converted to the corresponding anions under basic conditions, can be regarded as proton acceptors which link different proton donors of the ancillary molecules of water or boric acid. In this way, an isolated hydrogen‐bonded tetramer is constructed in salt 1 and a ribbon is constructed in salt 2 . The tetramers and ribbons are then packed in a repeating manner to generate various host frameworks, and the tetrapropylammonium guest counter‐ions are contained in the cavities of the host lattices to give the final stable crystal structures. In these two salts, although the host anion and guest cation are the same, the difference in the ancillary small molecules results in different structures, indicating the significance of ancillary molecules in the formation of crystal structures.     

Determination,residue and risk assessment of trifloxystrobin,trifloxystrobin acid and tebuconazole in Chinese rice consumption

A simple and rapid analytical method for the detection of trifloxystrobin, trifloxystrobin acid and tebuconazole in soil, brown rice, paddy plants and rice hulls was established and validated by liquid chromatography with tandem mass spectrometry. Acceptable linearity (R² > 0.99), accuracy (average recoveries of 74.3–108.5%) and precision (intra- and inter-day relative standard deviations of 0.9–8.8%) were obtained using the developed determination approach. In the field trial, the half-lives of trifloxystrobin and tebuconazole in paddy plants were 5.7–8.3 days in three locations throughout China, and the terminal residue concentrations of trifloxystrobin and tebuconazole were <100 and 500 μg/kg (maximum residue limits set by China), respectively, at harvest, which indicated that, based on the recommended application procedure, trifloxystrobin and tebuconazole are safe for use on rice. The risk assessment results demonstrated that, owing to risk quotient values of both fungicides being <100%, the potential risk of trifloxystrobin and tebuconazole on rice was acceptable for Chinese consumers. These data could provide supporting information for the proper use and safety evaluation of trifloxystrobin and tebuconazole in rice.     

Curing behavior and properties of high biosourced epoxy resin blends based on a triepoxy monomer and a tricarboxylic acid hardener from 10-undecenoic acid

Renewable propane-1,2,3-triyl tris(9-(oxiran-2-yl) nonanoate) (EGU, 100 wt% biogenic) and a tricarboxylic acid triglyceride (CGTU) hardener (85.7 wt% biogenic) were synthesized from 10-undecenoic acid (10-UDA) and used to produce epoxy resins with 52–92 wt% biobased carbon. CGTU was prepared by thermally activated thiol-ene coupling of thioglycolic acid onto propane-1,2,3-triyl tris(undec-10-enoate), (GUD) in the absence of solvent. The characterized CGTU was used as a green hardener of blends based on EGU and a conventional bisphenol A-based epoxy pre-polymer (DGEBA) at various mass percentages (0–100 wt%) with an stoichiometric epoxy/acid equivalent ratio. Calorimetric studies revealed higher peak temperature, lower reaction heats, and longer gelation times in resins with high EGU proportion, evidencing the lower reactivity of aliphatic EGU compared with aromatic DGEBA. Cured resins were yellowish transparent rubber-like materials with glass transition temperatures (Tg) varying from −14 °C to −42 °C and tensile strength in the range of 1750 kPa–790 kPa, for 0 and 100 wt % EGU, respectively. The soluble fraction of all resins was less than 4.3%, reflecting a high level of crosslinking. Thermosets with high biobased content showed both UV-light protection and visible light transparency.     

The effect of triethyl citrate on the dispersibility and water vapor sorption behavior of polylactic acid/zeolite composites

The aim of this study was to investigate the water vapor adsorption behavior and mechanical properties of poly (lactic acid) (PLA)/zeolite (5, 10, or 15 phr) composites prepared with triethyl citrate (TEC; 20 phr) via a melting process. TEC was used to improve the flexibility of the PLA and the dispersibility of the zeolite in TEC-zeolite suspensions that were ultra-sonicated. It was found that zeolite was uniformly dispersed in the PLA matrix, and the interfacial adhesion between the PLA matrix and zeolite was enhanced by TEC. In addition, the tensile strengths and Young's modulus of the composites improved with increasing zeolite content. The PLA/zeolite composites prepared with TEC had increased water vapor permeability and contact angles compared to neat PLA and standard PLA/zeolite due to the presence of TEC. In particular, TEC accelerated the hydrolysis of the PLA surface in a high humidity environment, resulting in an improvement in water vapor sorption capacity. At the same zeolite content of 15 phr, the equilibrium moisture content (EMC) values of PLA/zeolite films prepared with TEC increased by up to 39.25 mg/g whereas those prepared without TEC only increased by up to 24.33 mg/g. The results suggest the possibility of applying PLA/zeolite films prepared with TEC as a flexible active packaging material.     

Production and characterization of elastomeric cardiac tissue-like patches for Myocardial Tissue Engineering

Cardiovascular disease remains the leading cause of death. Damaged heart muscle is the etiology of heart failure. Heart failure is the most frequent cause of hospital and emergency room admissions. As a differentiated organ, current therapeutics and techniques can not repair or replace the damaged myocardial tissue. Myocardial tissue engineering is one of the promising treatment modalities for repairing damaged heart tissue in patients with heart failure. In this work, random Polylactic acid (PLA), Polylactic acid/Polyethylene glycol (PLA/PEG) and random and aligned Polylactic acid/Polyethylene glycol/Collagen (PLA/PEG/COL) nanofiber patches were successfully produced by the electrospinning technique. In vitro cytotoxic test (MTT), morphological (SEM), molecular interactions between the components (FT-IR), thermal analysis (DSC), tensile strength and physical analysis were carried out after production. The resulting nanofiber patches exhibited beadless and smooth structures. When the fiber diameters were examined, it was observed that the collagen doped random nanofiber patches had the lowest fiber diameter value (755 nm). Mechanical characterization results showed that aligned nanofiber patches had maximum tensile strength (5.90 MPa) values compared to PLA, PLA/PEG, and PLA/PEG/COL (random). In vitro degradation test reported that aligned patch had the highest degradation ratio. The produced patches displayed good alignment with tissue on cardiomyocyte cell morphology studies. In conclusion, newly produced patches have noticeable potential as a tissue-like cardiac patch for regeneration efforts after myocardial infarction.     

Purification of hyaluronidase as an anticancer agent inhibiting CD44

Hyaluronidase (Hyal) can be employed to accomplish a diversity of complications related to hyaluronic acid (HA). Hyal contains some classes of catalysts that cleave HA. This enzyme is detected in several human tissues as well as in animal venoms, pathogenic organisms and cancers. Destructive cancer cells regularly increase the CD44 receptor existing in a cell membrane. This receptor acts as an exact receptor for HA, and HA is recognized to motivate the migration, spread, attack and metastasis of cancer cells. Nearly all of the methods used to purify Hyal are highly costly and not proper for industrial applications. This survey aims to review different methods of Hyal purification, which acts as an anticancer agent by degrading HA in tissues and thus inhibiting the CD44–HA interaction. Hyal can be successfully employed in the management of cancer, which is associated with HA–CD44. This review has described different methods for Hyal purification to prepare an origin to develop a novel purification technique for this highly appreciated protein. Using multiple columns is not applicable for the purification of Hyal and thus cannot be used at the industrial level. It is better to use affinity chromatography of anti-Hyal for Hyal with one-step purification.